Temel Ferritik Çelikler

X6Cr13 – (1.4000) / X7Cr14 / SUS410S / Z6C13 / 403S17 / 2301 / 08KH13 / 0Cr13

 

Uygulama Bilgileri

 


Genel Kimliği

X6Cr13 – 1.4000

Grade X2CrTi12
Number 1.4512

Eş Değer Referansları

X6Cr13 – 1.4000

EU – EN X6Cr13
USA S41008
France, AFNOR Z6C13

Z6C12
England, BS 403S17
Japan, JIS SUS410S
Germany, DIN, WNr X7Cr14
Italy, UNI X6Cr13
China, GB 0Cr13
Sweden, SS 2301
Poland, PN 0H13
Czechia, CSN 17020
Russia, GOST 08KH13

Standartlar

X6Cr13 – 1.4000

Standart 1 EN 10088-2: 2005
Standart 2 EN 10088-3: 2005
Standart 3 EN 10088-1: 2005

Kimyasal Kompozisyonu

X6Cr13 – 1.4000

C max 0.08
Si max 1.00
Mn max 1.00
P max 0.040
S max 0.015
Cr 12 – 14

Mekanik Özellikleri

X6Cr13 – 1.4000

Rm – Tensile strength (MPa) (+A) 400 – 600

X6Cr13 – 1.4000

Rp0.2 0.2% Geçirmezlik Direnci (MPa) (+QT650) 220 – 240

X6Cr13 – 1.4000

A – Min. elongation at fracture (%) (+A) 19

X6Cr13 – 1.4000

Brinell Hardness (HB) (+A) 200

Hassas Kesim ve Zamanında Teslim