Temel Ostenitik Çelikler

X10CrNi18-8 – (1.4310) / 301 / X12CrNi17-7 / SUS301 / Z11CN18-08-09 / 301S21-26 / 2331 / X9CrNi18-8

 

Uygulama Bilgileri

 


Genel Kimliği

X10CrNi18-8 – 1.4310

Grade X10CrNi18-8
Number 1.4310
Sınıfı Temel Ostenitik Çelikler

Eş Değer Referansları

X10CrNi18-8 – 1.4310

USA 301
Germany, DIN X12CrNi17-7
Japan, Jis SUS301
France, AFNOR Z11CN18-08 Z11CN18-09
England, BS 301S21 302S26
Sweden, SS 2331
Inter, ISO X9CrNi18-8

Standartlar

X10CrNi18-8 – 1.4310

Standart 1 EN 10088-2: 2005
Standart 2 EN 10088-3: 2005
Standart 3 EN 10151: 2003
Standart 4 EN 10263-5: 2001
Standart 5 EN 10088-1: 2005

Kimyasal Kompozisyonu

X10CrNi18-8 – 1.4310

C 0.50 – 0.15
Si max 2.00
Mn max 2.00
Ni 6 – 9.5
P max 0.045
S max 0.015
Cr 16 – 19
Mo max 0.8
N max 0.11

Mekanik Özellikleri

X10CrNi18-8 – 1.4310

Rm – Tensile strength (MPa) (+A) 500 – 750
Rm – Tensile strength (MPa) (+AT+C) 850 – 890

X10CrNi18-8 – 1.4310

Rp0.2 0.2% Geçirmezlik Direnci (MPa) (+A) 195 – 250

X10CrNi18-8 – 1.4310

A – Min. elongation Lo = 80 mm (%) (+A) 40

X10CrNi18-8 – 1.4310

Nominal Kalınlık (mm) 2 – 25
Z – Reduction in cross section on fracture (%) 60 – 65

X10CrNi18-8 – 1.4310

Birinel Sertlik (HB) (+A): 230