Yüksek Dirence Dayanıklı Ostenitik Çelikler

X2CrNiMo18-14-3 – (1.4435) / 316L TP316L / 00Cr17Ni14Mo2 / Z3CND17-12-03 / SUS316L

 

Uygulama Bilgileri

 


Genel Kimliği

X2CrNiMo18-14-3 – 1.4435

Grade X2CrNiMo18-14-3
Number 1.4435

Eş Değer Referansları

X2CrNiMo18-14-3 – 1.4435

USA 316L TP316L
Germany DIN X2CrNiMo18-14-3
Japan, JIS SUS316L
France, AFNOR Z3CND17-12-03

Z3CND18-14-03
England, BS 316S13
Italy, UNI X2CrNiMo17-13
China, GB 00Cr17Ni14Mo2
Sweden, SS 2353
Czechia, CSN 17350
Finland, SFS 752
Russia, GOST 03KH17N14M3
Inter, ISO Type19a

Standartlar

X2CrNiMo18-14-3 – 1.4435

Standart 1 EN 10088-2: 2005
Standart 2 EN 10088-3: 2005
Standart 3 EN 10028-7: 2007
Standart 4 EN 10222-5: 2000
Standart 5 EN 10216-5: 2014
Standart 6 EN 10217-7: 2005
Standart 7 EN 10296-2: 2005
Standart 8 EN 10253-3: 2008
Standart 9 EN 10253-4: 2008
Standart 10 EN 10272: 2007
Standart 11 EN 10250-4: 2000
Standart 12 EN 10297-2: 2005
Standart 13 EN 10088-1: 2005
Standart 14 EN 10088-5: 2009
Standart 15 EN 10088-4: 2009

Kimyasal Kompozisyonu

X2CrNiMo18-14-3 – 1.4435

C max 0.03
Si max 1.00
Mn 2.00
Ni 12.5 – 13
P max 0.045
S max 0.015
Cr 17 – 19
Mo 2.5 – 3
N max 0.11

Mekanik Özellikleri

X2CrNiMo18-14-3 – 1.4435

Rm – Tensile strength (MPa) (+A) 490 – 700
Rm – Tensile strength (MPa) (+AT) 490 – 690

X2CrNiMo18-14-3 – 1.4435

Rp0.2 0.2% Geçirmezlik Direnci (MPa) (+A) 190 – 240
Rp0.2 0.2% Geçirmezlik Direnci (MPa) (+AT) 190 – 200

X2CrNiMo18-14-3 – 1.4435

KV – Impact energy (J) longitud +20° – 60 +196° – 60
KV – Impact energy (J) longitud +20° – 100

X2CrNiMo18-14-3 – 1.4435

A – Min. elongation at fracture (%) (+A) 30 – 45
A – Min. elongation at fracture (%) longitud, (+AT) 40

X2CrNiMo18-14-3 – 1.4435

Birinel Sertlik (HB) (+A): 215
Birinel Sertlik (HB) (+AT): 200