Derin Sıvamalık ve Manyetik Olmayan Ostenitik Çelikler

X2CrNiN23-4 – (1.4362) / S32304 / Z3CN23-04Az / 2327 / 03KH23N6

 

Uygulama Bilgileri

 


Genel Kimliği

X2CrNiN23-4 – 1.4362

Grade X2CrNiN23-4
Number 1.4362

Eş Değer Referansları

X2CrNiN23-4 – 1.4362

USA S32304
France, AFNOR Z3CN23-04Az
Sweden, SS 2327
Russia, GOST 03KH23N6

Standartlar

X2CrNiN23-4 – 1.4362

Standart 1 EN 10088-2: 2005
Standart 2 EN 10088-3: 2005
Standart 3 EN 10028-7: 2007
Standart 4 EN 10216-5: 2014
Standart 5 EN 10217-7: 2005
Standart 6 EN 10296-2: 2005
Standart 7 EN 10253-3: 2008
Standart 8 EN 10253-4: 2008
Standart 9 EN 10272: 2007
Standart 10 EN 10263-5: 2001
Standart 11 EN 10250-4: 2000
Standart 12 EN 10297-2: 2005
Standart 13 EN 10088-1: 2005
Standart 14 EN 10088-4: 2009
Standart 15 EN 10088-5: 2009

Kimyasal Kompozisyonu

X2CrNiN23-4 – 1.4362

C max 0.3
Si max 1.00
Mn max 2.00
Ni 3.5 – 5.5
P max 0.035
S max 0.015
Cr 22 – 24
Mo 0.1 – 0.6
N 0.05 – 0.2
Cu 0.1 – 0.6

Mekanik Özellikleri

X2CrNiN23-4 – 1.4362

Rm – Tensile strength (MPa) (+A) 600 – 850
Rm – Tensile strength (MPa) (+AT) 600 – 820

X2CrNiN23-4 – 1.4362

Rp0.2 0.2% Geçirmezlik Direnci (MPa) (+A) 400 – 450
Rp0.2 0.2% Geçirmezlik Direnci (MPa) (+AT) 400

X2CrNiN23-4 – 1.4362

KV – Impact energy (J) transverse (+A) +20° – 90 -40° – 40
KV – Impact energy (J) longitud (+A) +20° 100 – 120
KV – Impact energy (J) longitud (+AT) +20° 120

X2CrNiN23-4 – 1.4362

A – Min elogation at fracture (%) (+A) 20 – 25
A – Min. elongation at fracture (%) transverse., (+AT) 25
A – Min. elongation at fracture (%) longitud., (+AT) 25

X2CrNiN23-4 – 1.4362

Birinel Sertlik (HB) (+A): 260
Birinel Sertlik (HB) (+AT): 290